Sika® Permacor®-1705
Sika® Permacor®-1705 is a solvent-borne 1-pack primer based on alkyd resin.
- Fast drying, universally applicable as primer with a great range of dry film thicknesses
Usage
Sika® Permacor®-1705 is used as an anti-corrosive primer for atmospheric exposed steel surfaces.Advantages
- Fast drying, universally applicable as primer with a great range of dry film thicknesses
Packaging
| Sika® Permacor®-1705 | 25 kg net., 3 l |
Sika® Thinner S | 25 l, 10 l and 3 l |
Colour
Red brown approx. RAL 8012
Product Details
APPROVALS / CERTIFICATES
- Tested and official approved primer for Sika® Unitherm® and Sika® Pyroplast® fire protection systems on steel.
Shelf life
Min. 2 years
Storage conditions
In originally sealed containers in a cool and dry environment.
Density
~1.4 kg/l
Solid content
~49 % by volume
~67 % by weight
Chemical Resistance
Resistant to weathering.
Temperature Resistance
Dry heat up to + 80°C
Application
Thinner
Sika® Thinner S
If necessary max. 3 % Sika® Thinner S may be added to adapt the viscosity.
Product Temperature
Min. + 5°C
Relative Air Humidity
Max. 85 %, except the surface temperature is significantly higher than the dew point temperature, it shall be at least 3 K above dew point.
Surface Temperature
Min. + 5°C
Waiting Time / Overcoating
| At + 20°C | Min. 16 h |
Drying time
Drying time at + 20°C
| Loadable after | ~16 h |
Final drying time
Depending on film thickness and temperature full hardness is achieved within 1 week.
Consumption
Theoretical material-consumption/VOC without loss for medium dry film thickness:
Dry film thickness | 40 μm | 80 μm |
Wet film thickness | 85 μm | 165 μm |
| Consumption | ~0.114 kg/m2 | ~0.229 kg/m2 |
| VOC | ~37.7 g/m2 | ~75.6 g/m2 |
SURFACE PREPARATION
Steel:
Blast cleaning to Sa 2 ½ according to ISO 12944, part 4.
Free from dirt, oil and grease.
MIXING
Sika® Permacor®-1705 is supplied ready for use.
Stir thoroughly prior to application.
APPLICATION
The method of application has a major effect on achieving uniform thickness and appearance. Spray application will give the best results. The indicated dry film thickness is easily achieved by airless spray. Adding solvents reduces the sag resistance and the dry film thickness. In case of application by roller or brush, additional applications may become necessary to achieve the required coating thickness, depending on type of construction, site conditions, colour shade etc. Prior to major coating operations a test application on site may be useful to ensure the selected application method will provide the requested results.
By brush and roller
Conventional high pressure spraying:
- Nozzle size 1.3 - 2.0 mm
- Pressure 4 - 6 bar
Airless-spraying:
- Pressure min. 150 bar
- Nozzle size 0.38 - 0.53 mm (0.015 - 0.021 inch)
- Spraying angle 40° - 80°
CLEANING OF EQUIPMENT
Sika® Thinner S